PA12
Polyamide 12 is one of the most commonly used materials in machining techniques due to its flexibility and mechanical qualities.
This polyamide is different from other materials due to its high mechanical properties and good heat resistance. A low level of water absorption, resistance to hydrocarbons and oils and its high resistance to chemical agents complete its range of really excellent properties.
This material is highly suitable for all mechanical applications that require high performance: from traction to alternating bending, as well as in the field of robotics and pneumatics.
Technical Data of the material and physical and chemical properties
Mechanical Properties | Test Method | English | Metric |
Tensile Strength | ASTM D638 | 6,237 psi | 43 MPa |
Tensile Modulus | ASTM D638 | 230 ksi | 1,568 MPa |
Elongation at Break | ASTM D638 | 14% | 14% |
Flexural Strength | ASTM D790 | 6,962 psi | 48 MPa |
Flexural Modulus | ASTM D790 | 201 ksi | 1,387 MPa |
IZOD Impact, notched (Method A, 23°C) | ASTM D256 | 0.6 ft-lb/in | 32 J/m |
IZOD Impact, un-notched (Method A, 23°C) | ASTM D256 | 6.3 ft-lb/in | 336 J/m |
Gardner Impact | ASTM D5420 | 2.0 ft-lb | 2.7 J |
Thermal Properties | Test Method | English | Metric |
Heat Deflection (HDT) @ 66 psi | ASTM D648 | 356°F | 180°C |
Heat Deflection (HDT) @ 264 psi | ASTM D648 | 203°F | 95°C |
Coefficient Thermal Expansion 0-50 °C | ASTM E831 | 45.9 μin/in°F | 82.6 μm/m°C |
Coefficient Thermal Expansion 85-145 °C | ASTM E831 | 99.6 μin/in°F | 179.2 μm/m°C |
Other | Test Method | Value | Available Colors | |
Shore Hardness (D) | D2240 | 73 |
|
|
Water absorption, % - 24 hours | D570 | 0.07 % | ||
Dielectric Strength | D149 | 17.3 kV/mm | ||
Dielectric Constant @ 1 Khz | D150 | 2.73 | ||
Dissipation Factor @ 1 Khz | D150 | 0.044 | ||
Specific Gravity | ASTM D792 | 1.00g/cm3 |